Carbon Fibre Sheet Twill Gloss Double sided A finish 1 to 6mm Thicknesses

•  
• RC Model Parts
•  
• Race Cars & Automotive
•  
• Drones
•  
• Industrial Robotics
•  
• Musical Instruments
•  
• Bikes
•  
• Furniture
•  

Specifications 

One of the key advantages of twill weave carbon fiber is its balance between flexibility and strength. Compared to plain weave carbon fiber, twill weave offers a slightly looser structure, allowing for better drapability over complex surfaces while maintaining excellent durability. The double-sided gloss finish is achieved through a specialized curing process, ensuring a smooth and mirror-like surface that resists scratches and UV damage. This makes it a preferred choice for high-performance applications such as car interiors, drones, and luxury consumer products.

The double-sided gloss finish not only enhances the visual appeal but also provides functional benefits. A smooth, glossy surface reduces air resistance, making it useful for aerodynamic applications. Additionally, the epoxy coating on both sides adds an extra layer of protection against environmental factors such as moisture, heat, and chemicals. This durability makes it a great material for both indoor and outdoor applications, where strength, lightweight properties, and aesthetics are required simultaneously.

Another significant benefit of carbon fiber sheets with a double-sided gloss twill weave is their versatility in manufacturing. These sheets can be easily cut, drilled, and shaped to fit custom applications. Whether used for structural reinforcement, decorative panels, or even DIY projects, the material is user-friendly while maintaining its integrity. Furthermore, its resistance to corrosion and fatigue makes it a long-lasting investment compared to traditional materials like aluminum or steel.

In industries such as automotive, marine, and aerospace, these carbon fiber sheets are highly valued for their combination of lightweight strength and premium appearance. Their high stiffness-to-weight ratio allows engineers and designers to create parts that are both functional and visually striking. Whether used for dashboards, exterior trims, or performance components, the double-sided gloss twill weave carbon fiber sheets offer an unmatched blend of beauty and durability, making them a top choice for professionals and hobbyists alike.

Technical Data for Carbon Fiber Sheet – Double-Sided Cosmetic Finish (Gloss Twill Weave, Prepreg)

1. Material Composition

• Fiber Type: High-strength carbon fiber (typically Toray T300, T700, or equivalent)
• Resin System: Epoxy-based prepreg (pre-impregnated with thermoset resin)
• Weave Style: Twill weave (2x2 or 4x4 pattern)
• Finish: Glossy on both sides (double-sided cosmetic finish)
• Curing Process: Autoclave, vacuum bagging, or oven curing

2. Mechanical Properties

• Tensile Strength: ~500-600 MPa (72,500-87,000 psi)
• Tensile Modulus: ~50-70 GPa (7.2-10.2 Msi)
• Flexural Strength: ~600-900 MPa (87,000-130,000 psi)
• Flexural Modulus: ~50-80 GPa (7.2-11.6 Msi)
• Interlaminar Shear Strength (ILSS): ~40-60 MPa (5,800-8,700 psi)

3. Physical Properties

• Density: ~1.5-1.6 g/cm³
• Fiber Volume Fraction (FVF): ~55-65%
• Thickness Options: 0.25mm (0.01") to 5mm (0.2") or custom sizes
• Standard Sheet Sizes: 200x300mm, 500x500mm, 1000x1000mm (custom sizes available)
• Surface Finish: High-gloss, UV-resistant clear epoxy on both sides

4. Thermal Properties

• Glass Transition Temperature (Tg): ~120-180°C (248-356°F), depending on resin system
• Operating Temperature: -50°C to +150°C (-58°F to 302°F)
• Thermal Conductivity: ~5-10 W/m·K (higher in fiber direction)

5. Additional Features

• High Strength-to-Weight Ratio: Significantly lighter than metals such as aluminum or steel
• Excellent Fatigue Resistance: Maintains strength over time under cyclic loading
• Corrosion & Chemical Resistance: Non-reactive to most chemicals and moisture
• Machinability: Can be cut, drilled, and shaped with appropriate tools