Foam Core Rohacell 31 IG-F PMI
Couldn't load pickup availability
https://www.ebay.co.uk/itm/314715573867
SPECIFICATION
Weight and Dimensions
Length | 625 | mm |
---|---|---|
Width | 312 | mm |
Thickness | 2 | mm |
Thickness Tolerance (+/-) | 0.5 | mm |
Product Data
Colour | White | |
---|---|---|
Density (Dry) | 32 | kg/m³ |
Mechanical Properties
Max Service Temp | 180 | °C |
---|---|---|
Tensile Strength | 1.0 | MPa |
Tensile Modulus | 36 | GPa |
Compressive Strength | 0.4 | MPa |
Plate Shear Strength | 0.4 | MPa |
Plate Shear Modulus | 13 | GPa |
Coefficient Linear Expansion | 50.3 | 10-6/K |
Elongation at Break | 3 | % |
Compressive Modulus | 17 | MPa |
Chemistry / Material | PMI |
---|
General Properties
Gross Weight | 0.01 | kg |
---|
Foam Core Rohacell 31 IG-F PMI stands out as a high-performance structural foam known for its exceptional strength, stiffness, and thermal stability. Comprising a closed-cell structure, this Rohacell variant offers superior mechanical properties, making it an ideal choice for demanding applications in aerospace, automotive, and industrial sectors. The foam's 31 IG-F designation denotes its compatibility with elevated temperature environments, ensuring reliability and performance in challenging operational conditions.
Rohacell 31 IG-F PMI finds extensive use in sandwich composite structures, where its lightweight nature and outstanding mechanical characteristics contribute to overall weight reduction without compromising structural integrity. This foam core is particularly favored in aerospace applications, forming an integral part of aircraft components like wings, fuselage panels, and interior structures. Its ability to withstand high temperatures and harsh environmental conditions positions it as a key material for industries seeking advanced solutions for lightweight, durable, and thermally stable composite structures