Mylar Release Film 125 Micron (914mm)
Couldn't load pickup availability
https://www.ebay.co.uk/itm/314715573867
SPECIFICATION
Product Data
Colour | White | |
---|---|---|
Type | Release Film | |
Format | Flat Film | |
Chemistry / Material | PET |
Weight and Dimensions
Film Thickness | 125 | μm |
---|---|---|
Width | 914 | mm |
Areal Weight | 173 | g/m² |
Mechanical Properties
Max Service Temp | 150 | °C |
---|---|---|
Tensile Strength | 180 | MPa |
Tensile Modulus | 3600 | MPa |
Elongation at Break | 150 | % |
General Properties
Gross Weight | 0.158 | kg |
---|---|---|
Brand | Dupont |
Release Film 125 Micron (914mm) is a versatile and essential component in composite manufacturing processes, particularly in the fabrication of composite structures and components. With a thickness of 125 microns and a width of 914mm, this release film serves as a reliable barrier during the curing process, preventing adhesion between the composite material and the mold surface. Its optimal thickness ensures effective release properties, facilitating the demolding of composite parts with intricate details and maintaining the integrity of the finished product.
The 914mm width of this release film makes it suitable for a variety of applications, accommodating different sizes and shapes of molds used in composite manufacturing. The release film's compatibility with various resins and composite materials enhances its adaptability across industries such as aerospace, automotive, and marine, where precision and quality are paramount. The 125-micron thickness strikes a balance between flexibility and durability, allowing for easy application and removal while providing the necessary protection during the curing process.
In addition to its functional aspects, Release Film 125 Micron (914mm) contributes to cost-effectiveness in composite production. Its optimized thickness and width reduce material wastage, making it an economical choice for manufacturers looking to enhance efficiency without compromising on quality. As a critical element in the composite fabrication workflow, this release film ensures a smooth and efficient demolding process, ultimately contributing to the production of high-quality composite components in diverse industries