Carbon Fibre Cloth 90g ProFinish Plain Weave 1k
Couldn't load pickup availability
https://www.ebay.co.uk/itm/314715573867
Carbon Fibre 90g ProFinish Plain Weave 1K Fabric is a lightweight and versatile composite material used in applications requiring a combination of strength, precision, and aesthetic appeal. This fabric is made from 1K carbon fiber tows, each tow containing 1,000 filaments. The plain weave structure, characterized by its checkerboard pattern, offers balanced mechanical properties and excellent drapability, making it suitable for intricate mold shapes. The ProFinish treatment enhances the fabric's workability, reducing fraying and distortion during handling and lamination processes.
SPECIFICATION
Product Data
| Width | 150 | mm |
|---|
Fabric Specification
| Fibre Specifics | Toray T300 1k | |
|---|---|---|
| Colour | Black | |
| Weave | 1 x 1 Plain | |
| Format | Woven Fabric | |
| Filament Count | 1k | |
| Fibre Type | Carbon Fibre | |
| Brand | Toray | |
| Ends | 7 | cm |
| Picks | 7 | cm |
| Fibre Orientation | 0, 90 |
Weight and Dimensions
| Thickness | 0.1 | mm |
|---|---|---|
| Consolidated Thickness | 0.1 | mm |
| Areal Weight | 90 | g/m² |
Fibre Properties
| Stabilisation | ProFinish | |
|---|---|---|
| UV Resistance | Fully UV Stable | |
| Density | 1.76 | g/cm³ |
| Filament Diameter | 7 | µm |
Compatible With
| Compatible With | Epoxy | Yes |
|---|---|---|
| Compatible With | Polyester | Yes |
| Compatible With | Vinylester | Yes |
Typical Laminate Properties
| Tensile Strength | 1860 | MPa |
|---|---|---|
| Tensile Modulus | 135 | GPa |
| Compressive Strength | 1470 | MPa |
| Flexural Strength | 1810 | MPa |
| Flexural Modulus | 125 | GPa |
| Interlaminar Shear Strength | 98.1 | MPa |
General Properties
| Gross Weight | 0.183 | kg |
|---|
One of the standout features of this fabric is its extremely low weight of 90g/m², making it ideal for projects where weight savings are critical. Despite its lightweight nature, it retains excellent tensile strength and stiffness, characteristics inherent to carbon fiber materials. This balance of low weight and high performance is essential in industries like aerospace, motorsports, and sporting goods, where even minor weight reductions can have a significant impact on performance and efficiency.
The plain weave pattern of the 90g ProFinish fabric provides consistent strength in both warp and weft directions. This bidirectional stability makes it particularly well-suited for load-bearing applications where forces are applied from multiple directions. Additionally, the plain weave design ensures good surface coverage and a uniform appearance, which is often desirable for visible composite components. The 1K tow size contributes to the fabric's fine texture, which is perfect for achieving a high-quality finish on smaller or more delicate components.
The ProFinish treatment adds a layer of practicality to the fabric. It minimizes fraying during cutting and handling, making the fabric easier to work with in manual layup processes. This feature reduces waste and ensures cleaner, more precise cuts, which are essential when working on intricate molds or detailed parts. ProFinish also improves the adhesion between the fabric and resin systems, resulting in superior laminate quality with fewer imperfections.
Overall, Carbon Fibre 90g ProFinish Plain Weave 1K Fabric is a premium choice for lightweight and high-performance composite applications. Its unique combination of a low weight, aesthetic plain weave pattern, and enhanced handling characteristics makes it an invaluable material for engineers and craftsmen alike. Whether used in aerospace panels, high-performance bicycles, or decorative carbon fiber parts, this fabric delivers the strength, precision, and elegance demanded by advanced composite projects.