Carbon Fibre Prepreg 150gsm Unidirectional 300mm Width Autoclave

In stock
Regular price £45.99 GBP inc. VAT
length

https://www.ebay.co.uk/itm/314715573867

SPECIFICATION

Fabric Specification
Fibre Specifics High Strength CF
Resin Matrix Epoxy
Brand XPREG
Fibre Type Carbon Fibre
Fibre Orientation Unidirectional
Weave Unidirectional
Colour Black
Type Component Prepreg
Filament Count 24K/50K
Format Unidirectional
Fibre Properties
Freezer-life (at -18°C) 12 Months
UV Resistance Good
Max Service Temp 130 °C
Filament Diameter 7 µm
Min Cure Temp 80 °C
Out-life (at 20°C) 30 Days
Max Cure Temp 120 °C
Typical Laminate Properties
Flexural Modulus 60.1 GPa
Tensile Strength 645 MPa
Flexural Strength 882 MPa
Interlaminar Shear Strength 69.8 MPa
Compressive Strength 615 MPa
Tensile Modulus 55.2 GPa
Tg Peak (DMA) 148 °C
Tg Onset (DMA) 140 °C
Weight and Dimensions
Areal Weight 150 g/m²
Consolidated Thickness 0.15 mm
Width 300 mm
Resin Weight 37 %
Suitable Uses
Suitable Uses Autoclave Prepreg Yes
General Properties
Gross Weight 0.46 kg
Brand XPREG

 

Unidirectional carbon fiber prepreg fabric weighing 150 grams is a high-performance composite material renowned for its exceptional strength-to-weight ratio and versatility in various industries. Comprising continuous carbon fibers aligned in a single direction and pre-impregnated with epoxy resin, this fabric offers engineers and manufacturers precise control over material properties, making it an ideal choice for applications demanding superior strength and stiffness. The unidirectional alignment of fibers ensures that the majority of the load is carried along the intended direction, optimizing mechanical performance and minimizing material waste.

Weighing 150 grams per square meter, this prepreg fabric strikes a balance between lightness and structural integrity. The controlled resin content in the prepreg simplifies the manufacturing process, as it eliminates the need for on-site resin application, reducing production time and ensuring consistent quality. Commonly used in aerospace, automotive, and sports equipment manufacturing, 150g unidirectional carbon fiber prepreg fabric empowers designers to create components with unparalleled strength and durability, contributing to the development of lightweight yet robust structures across various engineering applications