Carbon Fibre Component Prepress 210g Twill 3k 2/2 1250mm Width Out of Autoclave
Couldn't load pickup availability
https://www.ebay.co.uk/itm/314715573867
SPECIFICATION
Fabric Specification
| Fibre Specifics | Pyrofil TR30S 3k | |
|---|---|---|
| Colour | Black | |
| Fibre Orientation | 0, 90 | |
| Type | Component Prepreg | |
| Resin Matrix | Epoxy | |
| Weave | 2 x 2 Twill | |
| Format | Woven Fabric | |
| Filament Count | 3k | |
| Fibre Type | Carbon Fibre | |
| Brand | XPREG | |
| Ends | 5 | /cm |
| Picks | 5 | cm |
Weight and Dimensions
| Width | 1250 | mm |
|---|---|---|
| Consolidated Thickness | 0.25 | mm |
| Areal Weight | 210 | g/m² |
| Resin Weight | 42 | % |
Fibre Properties
| Min Cure Temp | 85 | °C |
|---|---|---|
| Max Cure Temp | 120 | °C |
| Max Service Temp | 115 | °C |
| Filament Diameter | 7 | µm |
| Out-life (at 20°C) | 30 | Days |
| Freezer-life (at -18°C) | 12 | Months |
| UV Resistance | Good |
Typical Laminate Properties
| Tensile Strength | 521 | MPa |
|---|---|---|
| Tensile Modulus | 55.1 | GPa |
| Compressive Strength | 483 | MPa |
| Flexural Strength | 777 | MPa |
| Flexural Modulus | 46.7 | GPa |
| Interlaminar Shear Strength | 64.7 | MPa |
| Tg Onset (DMA) | 121 | °C |
| Tg Peak (DMA) | 135 | °C |
General Properties
| Gross Weight | 0.73 | kg |
|---|---|---|
| Brand | XPREG |
Carbon fiber 210g twill component prepreg fabric stands at the forefront of advanced materials, offering a meticulously engineered solution for lightweight and high-strength applications. Weighing 210 grams per square meter, this prepreg fabric features a twill weave pattern, characterized by its distinctive diagonal structure. This weaving technique enhances the fabric's flexibility and conformability, allowing it to conform seamlessly to complex shapes and curves. The prepreg aspect indicates that the carbon fibers are pre-impregnated with a resin matrix, ensuring consistent resin distribution and facilitating ease of handling during the manufacturing process. The 210g weight strikes a balance between structural integrity and weight reduction, making it a versatile choice for various industries, including aerospace, automotive, and sporting goods.
In applications where performance and precision are paramount, carbon fiber 210g twill component prepreg fabric excels. The twill weave not only enhances the fabric's drapeability but also contributes to its aesthetic appeal. The 210g weight ensures a robust yet lightweight construction, making it an ideal choice for components that demand both strength and agility. This prepreg fabric finds its niche in the production of components such as automotive body panels, aircraft interiors, and high-performance sporting equipment, where the combination of weight savings, durability, and a visually striking twill pattern plays a pivotal role in achieving optimal results